1、选用抗静电剂对织物进行树脂整理。用抗静电剂对织物进行树脂整理，经过浸轧、焙烘而粘附在合成纤维织物的表面，使织物具有一定的抗静电效果。这种方法现在只用于民用服装以克服衣服缠身、火花放电、污染吸灰等静电现象。

1. Use anti-static agents for resin finishing of fabrics. Resin finishing of fabrics with anti-static agents, followed by immersion rolling and baking to adhere to the surface of synthetic fiber fabrics, giving the fabrics a certain anti-static effect. This method is now only used for civilian clothing to overcome static electricity phenomena such as clothing entanglement, spark discharge, pollution and dust absorption.

2、在涤纶或锦纶聚合物的内部添加抗静电剂，如磷酸脂、磺酸盐等表面活性剂或引入第三单体以取得耐久性抗静电纤维。由于添加剂的抗静电剂大多数是遇碱会起反应或分解的表面活性剂，因此在织物整理或洗涤时忌用碱性洗涤剂，以防止影响抗静电效果，这种纤维适宜作无尘服、无菌衣，也可用于民用服装等。

2. Add anti-static agents such as phosphoric acid esters, sulfonates, and other surfactants or introduce third monomers inside polyester or nylon polymers to obtain durable anti-static fibers. Due to the fact that most of the anti-static agents used in additives are surfactants that react or decompose when exposed to alkali, alkaline detergents should be avoided during fabric finishing or washing to prevent affecting the anti-static effect. This fiber is suitable for use as dust-free clothing, sterile clothing, and can also be used for civilian clothing.

3、在普通织物中混入导电纤维。在普通织物中混入导电纤维，这种防静电织物由于不受所在环境的影响，现已普遍被接受和认可。这种防静电织物的抗静电性能与导电纤维的种类和导电成分(金属、石墨、炭黑等)在纤维中的分部情况，又分为几种不同类型。其中含有炭黑、石墨等导电成分的其它复合型导电纤维可以直接用于织造的长丝，经纱中每隔一定间距(如1.5 cm左右)嵌入一根导电长丝，即可获得很好的抗静电效果，是目前用来织造防静电工作服面料的导电纤维。

3. Mixing conductive fibers into ordinary fabrics. Mixing conductive fibers into ordinary fabrics, this anti-static fabric is widely accepted and recognized because it is not affected by the environment it is in. The anti-static performance of this anti-static fabric is divided into several different types based on the type of conductive fibers and the distribution of conductive components (metal, graphite, carbon black, etc.) in the fibers. Other composite conductive fibers containing conductive components such as carbon black and graphite can be directly used for weaving long filaments. A conductive long filament can be embedded in the warp yarn at regular intervals (such as about 1.5 cm) to achieve good anti-static effect, making it the best conductive fiber currently used for weaving anti-static workwear fabrics.